| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point (Decomposition) | °C | 427 - 482 |
| Density | g mL-1 | 1.44 - 1.45 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | -2.2 - (-4.9) (along axis) |
| Thermal Conductivity | W / mK | 2.5 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | |
| Tensile Strength, Break at 23 C | MPa | 2400 - 3600 |
| Elongation, Yield | % | |
| Elongation, Break | % | 1.9 - 4.4 |
| Tensile Modulus at 23 C | GPa | 60 - 120 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | ||
| Dielectric Constant @ 1 MHz | n/a | ||
| Dissipation Factor @ 1 MHz | n/a |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Shrinkage | % | < 0.1 | |
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 3.2 - 6.5 |